model numarası.: ASTM A213
Marka: ZENGİNLERE
Ambalaj: Demetler halinde Ahşap kutularda
Verimlilik: 60000 Tons per Year
Ulaşım: Ocean,Land,Air
Menşe yeri: Çin
Desteklemek: 60000 Tons per Year
Sertifika: ISO 9001 ISO 14001 TS 16949 EN 10204.3.1 LR KR
HS Kodu: 7304419000
Liman: Ningbo,Shanghai
Ödeme şekli: L/C,T/T,D/P,Paypal,Money Gram,Western Union
Incoterm: FOB,CFR,FCA,CPT
Kazan Tavlı Turşu Paslanmaz Dikişsiz Çelik Boru
Product Name | ASTM A213 316Ti stainless steel seamless tube |
Material | stainless steel 316Ti |
Process | cold drawn, cold rolling |
Standard | A213, A312, A269, A511 |
Grade | 304, 304L, 316L, 321, 347H, S31803, 904L |
Size | 6 - 610 mm |
Length | 800mm - 20000 mm |
Used | bolier, heat exchanger |
Dikişsiz paslanmaz kazan borusu toleransı:
Production Method | Size(mm) | Tolerance | |
Hot Rolling(Extrusion) | OD | ≤140 | ±1.25% |
>140 | ±1.0% | ||
WT | ≤10 | ±12.5% | |
>10 | ±15% | ||
Cold Drawn(Cold Rolled) | OD | 8~30 | ±0.20mm |
>30~50 | ±0.30mm | ||
>50 | ±0.8% | ||
WT | 1.0~3 |
+12% -10% |
|
>3.0 |
±10% |
Standard | ASME SA213/ASTM A213, ASTM A269/ASME SA269, ASME SA312/ASTM A312, ASME249/ASTM A249, ASME SA511/ASTM A511, ASTM A270/ASME SA270, EN10216-5,EN10305-1, EN10217-5, DIN 17175, DIN 2448, DIN 6258, GOST 8731, JIS G3463, JIS G3462, JIS G3455, JIS G3459 etc. |
Material | TP304, TP304L, TP304H, TP304LN, TP314, TP316, TP316L, TP316LN, TP321, TP321H, TP310, TP310S, TP317, TP317L, TP347, TP347H, N08904, 904l, 253MA(S30815), 254SMO(S31254). |
Type | Seamless / SML |
O.D | 6-530mm |
W.T | 0.7-50mm |
Length | 0-38000mm |
Technique | Cold Finished (Cold Drawing and Cold Rolling), Hot Finished (Hot Extrusion) |
Ends | PE/Plain Ends, BE/Beveled Ends |
316 kalite paslanmaz çelik için kompozisyon çeşitleri.
Grade |
|
C | Mn | Si | P | S | Cr | Mo | Ni | N |
---|---|---|---|---|---|---|---|---|---|---|
316 | Min | - | - | - | 0 | - | 16.0 | 2.00 | 10.0 | - |
Max | 0.08 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
316L | Min | - | - | - | - | - | 16.0 | 2.00 | 10.0 | - |
Max | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
316H | Min | 0.04 | 0.04 | 0 | - | - | 16.0 | 2.00 | 10.0 | - |
max | 0.10 | 0.10 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | - |
316 kalite paslanmaz çeliğin mekanik özellikleri.
Grade | Tensile Str (MPa) min | Yield Str 0.2% Proof (MPa) min | Elong (% in 50 mm) min | Hardness | |
---|---|---|---|---|---|
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 | 515 | 205 | 40 | 95 | 217 |
316L | 485 | 170 | 40 | 95 | 217 |
316H | 515 | 205 | 40 | 95 | 217 |
316 kalite paslanmaz çelik için tipik fiziksel özellikler.
Grade | Density(kg/m3) | Elastic Modulus (GPa) | Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100 °C (J/kg.K) | Elec Resistivity (nΩ.m) | |||
---|---|---|---|---|---|---|---|---|---|
0-100 °C | 0-315 °C | 0-538 °C | At 100 °C | At 500 °C | |||||
316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
316 kalite paslanmaz çelik için kalite özellikleri.
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
---|---|---|---|---|---|---|---|
BS | En | No | Name | ||||
316 | S31600 | 316S31 | 58H, 58J | 1.4401 | X5CrNiMo17-12-2 | 2347 | SUS 316 |
316L | S31603 | 316S11 | - | 1.4404 | X2CrNiMo17-12-2 | 2348 | SUS 316L |
316H | S31609 | 316S51 | - | - | - |
Mekanik özellik
Çelik borunun boyuna mekanik özelliklerinin ısıl işlemi standarda göre yapılmalıdır.
Material |
Tensile strength MPa ≥ |
Yield Strength MPa ≥ |
Elongation % ≥ |
0Cr18Ni9 | 520 | 205 | 35 |
1Cr19Ni9 | 520 | 205 | 35 |
0Cr19Ni10 | 480 | 175 | 35 |
1Cr18Ni9Ti | 550 | 205 | 40 |
0Cr18Ni12Mo2Ti | 530 | 205 | 35 |
0Cr26Ni5Mo2 | 590 | 390 | 18 |
1Cr17 | 410 | 245 | 20 |
00Cr27Mo | 410 | 245 | 20 |
1Cr25Ti | 440 | 245 | 17 |
Sertlik:
WT ≥2 mm olan tüpler için Rockwell sertlik testleri yapılmalıdır.
Dikişsiz kazan borularının testleri:
1. Eğme Testi:
OD ≤22mm olduğunda tüpler bükme testine girmelidir. Bükülme açısı 90 derecedir ve bükülme yarıçapı, çelik borunun dış çapının 6 katıdır.
2. Hidrolik test;
Girdap akımı testi, hidrolik testler yerine ultrasonik test kullanılabilir. Girdap akımı testi yapıldığında, GB / T 7735-1995 Gr. A takip edilmelidir; ultrasonik test sırasında, GB / T 5777-1996 Gr. C8 takip edilmelidir.
3. Düzleştirme testi
4. Flanş testi
5. Testi genişlet
Ürün kategorileri : Dikişsiz Çelik Borular
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.